  • Thumbnail Image
    PublicationEmbargo
    Decay in Mechanical Properties of Catalyst Coated Membranes Subjected to Combined Chemical and Mechanical Membrane Degradation
    (Wily, 2014-11-28) Rajapakse, R. K. N. D; Wang, G. G; Lauritzen, M; Kjeang, E; Lim, C; Ghataurah, J; Khorasany, R. M. H; Goulet, M. A; Alavijeh, A. S
    The mechanical stability of catalyst coated membranes (CCMs) is an important factor for the overall durability and lifetime of polymer electrolyte fuel cells. In this article, the evolution of the mechanical properties of degraded CCMs is comprehensively assessed. A combined chemical and mechanical accelerated stress test (AST) was applied to simulate field operation and rapidly generate partially degraded CCM samples for tensile and expansion experiments under both room and fuel cell conditions. The tensile results indicated significant reductions in ultimate tensile strength, toughness, and fracture strain as a function of AST cycles, accompanied by a mild increase in elastic modulus. The increased brittleness and reduced fracture toughness of the CCM, caused primarily by chemical membrane degradation, is expected to play an important role in the ultimate failure of the fuel cell. The expansion tests revealed a linear decay in hygrothermal expansion, similar in magnitude to the loss of mechanical strength. The decline in CCM sensitivity to environmental changes leads to non-uniform swelling and contraction that may exacerbate local degradation. Interestingly, the hygrothermal expansion in the late stages of degradation coincided with the fracture strain, which correlates to in situ development of fractures in chemically weakened membranes.
  • Thumbnail Image
    PublicationEmbargo
    Mechanical degradation of fuel cell membranes under fatigue fracture tests
    (Elsevier, 2015-01-01) Khorasany, Ramin M.H; Alavijeh, A. S; Kjeang, E.; Wang, G.G.; Rajapakse, R. K. N. D
    The effects of cyclic stresses on the fatigue and mechanical stability of perfluorosulfonic acid (PFSA) membranes are experimentally investigated under standard fuel cell conditions. The experiments are conducted ex-situ by subjecting membrane specimens to cyclic uniaxial tension at controlled temperature and relative humidity. The fatigue lifetime is measured in terms of the number of cycles until ultimate fracture. The results indicate that the membrane fatigue lifetime is a strong function of the applied stress, temperature, and relative humidity. The fatigue life increases exponentially with reduced stresses in all cases. The effect of temperature is found to be more significant than that of humidity, with reduced fatigue life at high temperatures. The maximum membrane strain at fracture is determined to decrease exponentially with increasing membrane lifetime. At a given fatigue life, a membrane exposed to fuel cell conditions is shown to accommodate more plastic strain before fracture than one exposed to room conditions. Overall, the proposed ex-situ membrane fatigue experiment can be utilized to benchmark the fatigue lifetime of new materials in a fraction of the time and cost associated with conventional in-situ accelerated stress testing methods.