Faculty of Humanities and Sciences
Permanent URI for this communityhttps://rda.sliit.lk/handle/123456789/4205
Browse
5 results
Search Results
Publication Open Access The photocatalytic and antibacterial activity of graphene oxide coupled CoOx /MnOx nanocomposites(Elsevier B.V., 2025-02) Liyanaarachchi, H; Thambiliyagodage, C; Jayanetti, M; Ekanayake, G; Wijayawardana, S; Samarakoon, UCoOx and MnOx metal oxide composites were fabricated via co-precipitation varying the Co:Mn (CM) weight ratio as 4:1, 2:1, 1:1, 1:2 and 1:4, and they hydrothermally coupled with 30 wt% of graphene oxide (GO). XRD analysis revealed the presence of Co3O4 and CoO, and Mn2O3 and Mn3O4 phases in pure CoOx and MnOx metal oxides, respectively. The irregularly shaped metal oxide nanocomposites comprised Co3O4, Mn2O3 and Mn3O4 phases and were immobilized on GO. The band gap values of the composites varied in the range of 1.86 – 2.22 eV. The highest photocatalytic activity with a rate constant of 3.5 × 10−3 min−1 was obtained with CMG (1:4). The total removal of MB increased by 55.8 % when CM (1:4) were coupled with GO. The rate of photocatalysis was dramatically increased in the presence of S2O82- and was decreased in the presence of EDTA and isopropyl alcohol. The effect of catalyst dosage was determined by varying the weight to 25, 50, 75, and 100 mg, and the dye concentration was varied in the range of 25, 50, 75 and 100 mg/L. The presence of Pb2+ and Rhodamine B decreased the photocatalytic activity, while it remained the same in the presence of Cl- and PO43- as co-pollutants. The photocatalytic activity of CMG (1:4) was reduced to 72 % upon using the catalyst for five cycles. All the synthesized nanocomposites exhibited greater sensitivity to the Gram-positive strain than the Gram-negative strains.Publication Open Access In vitro release kinetics of bioactive compounds (gallic acid, ellagic acid, and eugenol) from chitosan polymer and the bioactivity of herb-loaded chitosan–CuO nanocomposites(Nature Research, 2025-10-13) Ekanayake, G; Wijayawardana, S; Jayanetti, M; Thambiliyagodage, C; Liyanaarachchi, H; Mendis, AThe biological efficacy of nanocomposites comprised of chitosan, CuO nanoparticles, and extracts of Phyllanthus emblica, and Syzygium aromaticum was studied. The study assessed the pH– and ionic strength-responsive controlled release of the bioactive compounds, gallic acid, ellagic acid and eugenol, from the chitosan biopolymer. Release data were fitted into zero-order, first-order, Korsmeyer–Peppas (KP), Peppas–Sahlin (PS), Higuchi, and Hixson–Crowell kinetic models to evaluate the release mechanism. According to KP and PS models (R2 ≥ 0.96), release was governed by quasi-Fickian diffusion (n < 0.43), where the diffusion occurs along with the polymer relaxation and swelling. P.emblica-coated chitosan (PeC) composite exhibited a burst release at acidic media conditions, and a quasi-Fickian diffusion at pH 5.5–7.4. Higher ionic strength caused salting-in effects for PeC in 0.4 M media, resulting in a transiently increased release. In acidic conditions, diffusion-controlled release was observed for S.aromaticum-coated chitosan (SaC) composite, with the optimal release at pH 4 media. Release was facilitated by hydrophobic nanochannels at elevated pH (8.5–10) and ionic strength of 0.5 M NaCl. The PS model’s relaxation contributions were significant at 0.4 M NaCl and 5 mg drug loading. Both composites demonstrated enhanced release at physiological conditions (0.1–0.2 M NaCl, pH 7.4). Sustained release of SaC was achieved in near-neutral/moderate ionic strength media, whereas PeC exhibited sustained release in acid/low ionic strength media. The PeC and SaC composites showed IC50 values of 10.78 µg/mL and 19.27 µg/mL for the DPPH radical scavenging ability, respectively. Recorded IC50 values for the egg albumin denaturation assay were 467 µg/mL and 390.44 µg/mL, respectively. The antibacterial activity against Escherichia coli, Pseudomonas aeruginosa, Klebsiella pneumoniae, and Staphylococcus aureus showed maximum inhibition zones of 11.83 ± 0.06 mm (Chitosan: CuO 1:2), 12.67 ± 0.20 mm (1:4), 16.50 ± 0.09 mm (1:4), and 11.83 ± 0.08 mm (4:1), respectively. Among the herbal-coated samples, SaC exhibited the highest activity of 23.67 ± 2.84 mm against E. coliPublication Open Access Fabrication of Naturally Derived Chitosan and Ilmenite Sand-Based TiO2/Fe2O3/Fe-N-Doped Graphitic Carbon Composite for Photocatalytic Degradation of Methylene Blue under Sunlight(MDPI, 2023-04-01) Mendis, A; Thambiliyagodage, C; Ekanayake, G; Liyanaarachchi, H; Jayanetti, M; Vigneswaran, Sfirst_pagesettingsOrder Article Reprints Open AccessArticle Fabrication of Naturally Derived Chitosan and Ilmenite Sand-Based TiO2/Fe2O3/Fe-N-Doped Graphitic Carbon Composite for Photocatalytic Degradation of Methylene Blue under Sunlight by Amavin Mendis 1,Charitha Thambiliyagodage 1,*ORCID,Geethma Ekanayake 1,Heshan Liyanaarachchi 1ORCID,Madara Jayanetti 1 andSaravanamuthu Vigneswaran 2,3,* 1 Faculty of Humanities and Sciences, Sri Lanka Institute of Information Technology, Malabe 10115, Sri Lanka 2 Faculty of Engineering and Information Technology, University of Technology Sydney, P.O. Box 123, Sydney, NSW 2007, Australia 3 Faculty of Sciences & Technology (RealTek), Norwegian University of Life Sciences, P.O. Box N-1432 Ås, Norway * Authors to whom correspondence should be addressed. Molecules 2023, 28(7), 3154; https://doi.org/10.3390/molecules28073154 Received: 15 March 2023 / Revised: 29 March 2023 / Accepted: 30 March 2023 / Published: 1 April 2023 (This article belongs to the Section Materials Chemistry) Download Browse Figures Versions Notes Abstract Fabrication of chitosan and ilmenite sand-based novel photocatalysts through the catalytic graphitization of chitosan is reported. Nanocomposites consisted of TiO2, Fe2O3 and Fe nanoparticles dispersed on a nitrogen-doped graphitic carbon framework. The surface area, pore volume and macropore structure of the carbon matrix is disturbed by the heterogeneously distributed nanoparticles. The extent of graphitization expanded with increasing metal loading as indicated by variation in the ID/IG ratio. The nanomaterial’s surface consists of Fe3+ and Ti4+, and graphitic, pyridinic and pyrrolic nitrogen were found in the carbon matrix. The band gap values of the composites varied in the 2.06–2.26 eV range. The photocatalytic activity of the synthesized nanomaterials was determined, and the highest rate constant for the photodegradation of methylene blue under sunlight was 4.4 × 10−3 min−1, which resulted with 10 mg/L MB and 25 mg of the best-performing catalyst. The rate constant rose with increasing concentrations of persulfate added to the medium. The rate constant greatly diminished with the addition of isopropyl alcohol as it scavenged hydroxyl radicals. The presence of co-pollutants including Pb2+, rhodamine B, PO43− and Cl− curtailed the rate of reaction. The activity reduced with an increasing number of uses of the catalyst.Publication Open Access Efficient photocatalysis of Cu doped TiO2/g-C3N4 for the photodegradation of methylene blue(Elsevier, 2023-03-06) Liyanaarachchi, H; Thambiliyagodage, C; Liyanaarachchi, C; Samarakoon, UThe release of dyes into normal water reservoirs has become a tremendous environmental problem and the development of methods to remove such dyes is essential. A novel photocatalyst was fabricated in which Cu doped to TiO2 was coupled with g-C3N4 (Cu-TiO2/g-C3N4) in different weight percentages as 10, 30 and 50%, hydrothermally. Pure TiO2 consisted of both Anatase and Rutile phases where slight lattice distortions were observed in the Cu-doped TiO2 as evidenced by the XRD and Raman analysis. Cu was present at 1.7% by weight respective to TiO2 according to the XRF analysis. Spherical and irregularly shaped aggregated Cu-doped TiO2 nanoparticles in the range of 15–55 nm were heterogeneously distributed on the g-C3N4 matrix as observed by TEM and SEM. The band gap of TiO2 (3.0 eV) was reduced to 2.67 upon doping with Cu. The band gap of g-C3N4 was found to be 2.81 eV and that of Cu-TiO2/g-C3N4 in different weight percentages were in the range of 2.82 to 2.88 eV. Synthesized photocatalysts were tested on the ability to degrade methylene blue under UV and Visible light. Cu-TiO2/50% g-C3N4 showed the highest rate constant (4.4 × 10-3 min−1) which is 5 and 9.8 times greater than TiO2 and g-C3N4, respectively. The rate constant decreased with the introduction of EDTA and Isopropyl alcohol as they scavenge holes and hydroxyl radicals, respectively. The photocatalytic activity of all the nanomaterials increased with the increasing concentration of persulfate due to the increasing concentration of SO4●- and OH● produced. Synthesized nanomaterials effectively adsorb methylene blue under dark conditions following the pseudo-second-order kinetics suggesting that methylene blue molecules were chemisorbed to the adsorbents. The adsorption rate constant resulting in the best-performing photocatalyst was 0.122 g mg−1 min−1. Hence, it is evident that Cu-TiO2/g-C3N4 can effectively degrade methylene blue.Publication Open Access Fabrication of dual Z-scheme g-C3N4/Fe2TiO5/Fe2O3 ternary nanocomposite using natural ilmenite for efficient photocatalysis and photosterilization under visible light(Elsevier, 2022-11-11) Thambiliyagodage, C; Liyanaarachchi, H; Kumar, A; Jayanetti, M; Usgodaarachchi, L; Lansakara, BThe advanced oxidation process is a prominent method available to remove dyes released to normal water reservoirs to alleviate water scarcity. We report the fabrication of novel g-C3N4/Fe2TiO5/Fe2O3 using natural ilmenite sand as the precursor of the metallic semi-conductors exploration of a heterostructure for photodegradation of methylene blue under sunlight. Ternary composites were synthesized by varying g-C3N4 with respect to Fe2TiO5/Fe2O3 and varying Fe2TiO5/Fe2O3 with respect to g-C3N4 where the varying component was varied as 8, 24 and 40%, respect to the constant material. The hybridization of the three semi-conductors has been confirmed by the microscopic, chemical, and structural analyses. X-ray diffraction patterns show the presence of all three g-C3N4, Fe2TiO5 and α-Fe2O3 while the transmission electronic microscopic and scanning electronic microscopic images show the heterogeneous distribution of the metal oxide nanoparticles on g-C3N4 matrix forming the composite. HRTEM images further reveal the junction of Fe2TiO5 and α-Fe2O3. X-ray photoelectron spectra show the existence of s-triazine and heptazine rings in the composites with Fe3+ and Ti4+ as the only oxidation states of Fe and Ti. Fe2TiO5/Fe2O3/40% g-C3N4 with bandgap of 2.63 eV calculated by diffuse reflectance UV-Visible spectroscopy showed the highest photocatalytic activity (0.009 min−1) being 1.3 times greater than the Fe2TiO5/Fe2O3 nanoparticles. Enhanced photocatalytic activity over the fabricated composites was observed due to the increased visible light absorption, efficient charge separation and improved charge transportation. g-C3N4 coupled with 40% Fe2TiO5/Fe2O3 showed the highest antibacterial activity against gram-negative E.Coli. The synthesis of dual Z-scheme g-C3N4/Fe2TiO5/Fe2O3 ternary composite provides new sights in developing novel photocatalysts using natural ilmenite sand for environmental applications.