The photocatalytic and antibacterial activity of graphene oxide coupled CoOx /MnOx nanocomposites

Abstract

CoOx and MnOx metal oxide composites were fabricated via co-precipitation varying the Co:Mn (CM) weight ratio as 4:1, 2:1, 1:1, 1:2 and 1:4, and they hydrothermally coupled with 30 wt% of graphene oxide (GO). XRD analysis revealed the presence of Co3O4 and CoO, and Mn2O3 and Mn3O4 phases in pure CoOx and MnOx metal oxides, respectively. The irregularly shaped metal oxide nanocomposites comprised Co3O4, Mn2O3 and Mn3O4 phases and were immobilized on GO. The band gap values of the composites varied in the range of 1.86 – 2.22 eV. The highest photocatalytic activity with a rate constant of 3.5 × 10−3 min−1 was obtained with CMG (1:4). The total removal of MB increased by 55.8 % when CM (1:4) were coupled with GO. The rate of photocatalysis was dramatically increased in the presence of S2O82- and was decreased in the presence of EDTA and isopropyl alcohol. The effect of catalyst dosage was determined by varying the weight to 25, 50, 75, and 100 mg, and the dye concentration was varied in the range of 25, 50, 75 and 100 mg/L. The presence of Pb2+ and Rhodamine B decreased the photocatalytic activity, while it remained the same in the presence of Cl- and PO43- as co-pollutants. The photocatalytic activity of CMG (1:4) was reduced to 72 % upon using the catalyst for five cycles. All the synthesized nanocomposites exhibited greater sensitivity to the Gram-positive strain than the Gram-negative strains.